priti®multidisc ZrO2 Multi Translucent

The new multi-talent provides you with ideal support on your individual path to highly esthetic and long-lasting dentures. Following the trend, a blank that combines the positive properties of the already established zirconia qualities 3Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body.
zirconium oxide qualities 3Y-TZP and the highly translucent 5Y-TZP.

Imagine mixing 2 different material classes ...

The result could be a unique raw material combination of high-strength and highly translucent ZrO2. We just did it! In combination with our new innovative TILLY philosophy, the result is a multi-talent that defines a completely new generation!

With priti®multidisc ZrO2 Multi Translucent you can fabricate individual restorations for the anterior and posterior region on natural abutments and implants.
The special feature: gradual color and translucency gradient combined with high flexural strength. This makes priti®multidisc ZrO2 Multi Translucent an unconditional and flexible choice for a particularly wide range of indications.

Indications:

• Customized restorations for the anterior and posterior region on natural tooth abutments and implants
• Highly esthetic monolithic, fully anatomical crowns, partial crowns and bridges up to 14 units
• Inlays, onlays, veneers and abutments
• Rapid sintering of restorations with up to 3 units

Facts:

• Zirconium dioxide type II, class 5 according to DIN EN ISO 6872
• Flexural strength: typical mean value ? 1,100 MPa
• Translucency gradient from <, 40 % to >, 49 %
• Thin wall thicknesses in the anterior region 0.4 mm and posterior region 0.6 mm for single crowns
• Precise margins and edges thanks to highly compacted material
• Veneering is possible with any ceramic material that is matched to the CTE 10 - 10-6 - K-1 of ZrO2
• Cross-batch color fidelity
• Homogeneous coloring
• Reproducible shades
• Biocompatible